I am rebuilding an older Barnett crossbow and I need to repair some wear damage to the sear. All of the trigger components are made from mild steel and have grooves worn in them. Ideally I would replicate all the damaged components in something more durable but there are some pretty complex parts to deal with. How well would hard silver solder likely hold up as a contact surface on the sear? Anyone ever done anything like this?
Durability of hard silver solder?
- Thread starter websterz
- Start date
Help Support Home Model Engine Machinist Forum:
Silver solder is not really that good for building up fillets so may not fill your grooves. It also won't take much wear, probably similar to a hard brass. Could you not build it up with weld?
Jason
Jason
kf2qd
Well-Known Member
- Joined
- Apr 1, 2008
- Messages
- 618
- Reaction score
- 91
I am not sure of a source, but another possibility would be to get some stellite wire (Stellite 6) and using a process a lot like brazing, put a drop of that on the end and then mill/grind to suit. The Stelite would not need to be hardened and would end up Rockwell 40-45.
I used to work for the company and have seen some of what can be done with those materials. There are other companies making the same product, depends on where you are as to what might be the available brand.
I used to work for the company and have seen some of what can be done with those materials. There are other companies making the same product, depends on where you are as to what might be the available brand.
Web.
What about an epoxy like JB Weld? All you would need to do is create a key on the surface apply a blob of the stuff on then you can machine back your profile. I have machined this stuff and it works well plus its color is the same as steel.
There is another more tough product called Zonenite harder than rhino droppings and keeps its form up to a temp of 1400 deg but I do not know its machining capabilities.
Al the best. Anthony.
What about an epoxy like JB Weld? All you would need to do is create a key on the surface apply a blob of the stuff on then you can machine back your profile. I have machined this stuff and it works well plus its color is the same as steel.
There is another more tough product called Zonenite harder than rhino droppings and keeps its form up to a temp of 1400 deg but I do not know its machining capabilities.
Al the best. Anthony.